cleavage fracture

解理断裂

双语例句

Fractographic observations showed that hydrogen could induce surface cracks for smooth specimens and a cleavage fracture pattern for notch specimens at RT. 破断面观察结果显示，在室温中，氢气会导致平滑试片在表面形成裂纹，而在凹槽试片中产生劈裂破坏形态。

Fracture measurements show that the mode attributed to cleavage fracture. 断口实验结果表明，接头断裂模式为解理断裂。

The cleavage fracture after hot pressing is ductile and quasicleavage fracture. 热压后的拉伸断口为韧窝与准解理混合断裂。

Cleavage fracture is a typical brittle fracture and also a process consisted of crack producing and spreading, and the mechanism is related to dislocation and crystalline grain. 解理断裂是典型的脆性断裂，解理断裂也是一个裂纹萌生和扩展的过程，其机制与位错和晶粒有关。

The cutting tool was characterized by intercrystalline fracture attributed to fatigue and partial cleavage fracture in the machining process. 聚晶金刚石刀具在加工过程中的磨损机理主要表现为具有疲劳磨损特征的沿晶断裂及局部解理断裂。

Studies indicate that fracture of cast irons is different from brittle cleavage fracture of steels. 研究结果表明，铸铁的断裂与钢的脆性解理断裂不同。

The local cleavage fracture stress is mainly determined by the length of the critical microcrack. 细观解理断裂应力主要由临界裂纹的长度决定。

Hydrogen induced cleavage fracture for Fe-3% si single crystal and polycrystals was investigated. 用Fe-3%Si单晶试样对氢致解理断裂进行了研究。

Moreover, to explain the cleavage fracture in ductile materials also needs the development of strain gradient theory. 以及为韧性材料中的解理断裂现象提供一种合理的解释，都需要发展应变梯度理论。

On the measurement and physical meaning of the cleavage fracture stress in steel 钢解理断裂应力的测量和物理意义

The fracture mainly originated from cavity, and the intergranular fracture was the leading fracture mode, besides the cleavage fracture and transgranular fracture. 孔洞和大颗粒硬质相为主要的断裂源，断裂方式以沿晶断裂为主，同时存在着解理断裂和穿晶断裂。

In this article the quantitative relationship between the microscopic structure and other basic mechanical properties of cleavage fracture and plastic fracture on one side and fracture toughness on the other is discussed. 本文讨论了解理断裂和塑性断裂的显微结构及其它基本力学性能与断裂韧性的定量关系。

Ring Cleavage of Tetrafluoroethylene Sulfite The rupture is brittle cleavage fracture. 亚硫酸四氟乙二醇酯的环断裂反应此属于解理和准解理脆性断裂。

The Effect of Notch Root Radius on the Cleavage Fracture Stress σ_f 缺口根半径对解理断裂应力σf的影响

Microcracks in cleavage fracture. 解理断裂的微观过程；

The nucleated cracks cannot propagate and the cleavage fracture cannot be triggered. 因此形核的裂纹因不能扩展而不能引发解理断裂。

The rupture is brittle cleavage fracture. 此属于解理和准解理脆性断裂。

The cleavage fracture of the notched specimens with various sizes and widths is mainly controlled by the criterion of normal stress. 不同尺寸和宽度的缺口试样的解理断裂主要由正应力判据控制。

The reliability of stress intensification factor of this steel and the characteristic distance of cleavage fracture have been discussed. 讨论了该钢在解理断裂时应力强化系数Qf值的可靠性和断裂特征问题。

The cleavage fracture stress of silicon steel is determined. 测定了各种硅钢的解理断裂应力，导出了硅钢零塑性温度NDT的表达式。

Cleavage fracture stress of dual phase steels has been measured with slow-bend test of blunt V-notch specimens. 用缺口棒四点弯曲法测定了双相钢的解理断裂应力σf；

Effects of Microstructure and Composition on Cleavage Fracture Stress and Fracture Toughness of Low Carbon-structural Steel 组织和成分因素对低碳结构钢解理断裂应力及断裂韧性的影响

Transgranular cleavage fracture is shown for the charged layer in tensile specimen. 拉伸试样表面充氢层的断口是穿晶解理断口。

The surface of delamination crack is of cleavage fracture appearance with large cleavage face. 分层裂纹表面为解理形貌，解理面较大。

And the TiAl matrix has a duplex microstructure, and the fracture mode is transgranular cleavage fracture. 通过多步热处理，可以得到双态组织和晶粒更为细小均匀的近γ组织的TiAl基体，复合材料的断裂模式转变为穿晶解理断裂。

The fractures of the alloys change from dimple to cleavage fracture with river pattern. 合金的断口形貌由韧窝向河流花纹状的解理形貌转变。

Relation of ductile-brittle transition temperature to microstructure parameter and size of cleavage fracture element in carbon steels 碳钢韧脆转变温度与组织参量和解理断裂单元尺寸的关系

Dimensions of the stress and crystalline have influence on cleavage fracture. 应力的大小和晶粒的尺寸影响解理断裂。

Fatigue crack propagates in transgranular manner and the surface of fatigue fracture shows cleavage fracture feature. 疲劳裂纹产生以后均以穿晶方式进行扩展，疲劳断口表面呈现解理断裂特征。